Extruded molds and methods for manufacturing composite truck panels

ABSTRACT

Extruded molds and methods for manufacturing composite structures using the extruded molds are disclosed. The molds may include recessed or raised longitudinal features to impart a corresponding shape to the molded composite structures. The composite structures may be panels used to construct cargo vehicles, for example.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Patent Application Ser. No. 62/245,503, filed Oct. 23, 2015, the disclosure of which is hereby expressly incorporated by reference herein in its entirety.

FIELD OF THE DISCLOSURE

The present disclosure relates generally to molds and methods for manufacturing composite structures using the molds. More particularly, the present disclosure relates to extruded molds and methods for manufacturing composite truck panels using the extruded molds.

BACKGROUND OF THE DISCLOSURE

Molds are used to manufacture composite truck panels. The molds themselves may be constructed of fiberglass, but these fiberglass molds are generally fragile and susceptible to wear and damage. Alternatively, the molds may be constructed of metal, but these metal molds are typically machined and expensive to manufacture.

SUMMARY OF THE DISCLOSURE

Extruded molds and methods for manufacturing composite structures using the extruded molds are disclosed. The molds may include recessed or raised longitudinal features to impart a corresponding shape to the molded composite structures. The composite structures may be panels used to construct cargo vehicles, for example.

According to an exemplary embodiment of the present disclosure, a mold is provided to form a composite structure, the mold including an extruded mold body having a mold surface upon which the composite structure is formed.

According to another exemplary embodiment of the present disclosure, a composite panel formed upon a mold body is provided, the composite panel including a first end, a second end, and a molded surface. The molded surface includes a first portion that is flat, a second portion that is flat, and a third portion that deviates from being flat, wherein the third portion extends entirely from the first end to the second end.

According to yet another exemplary embodiment of the present disclosure, a method of manufacturing a composite structure is provided, the method including providing an extruded mold body having a mold surface, and forming the composite structure upon the mold surface.

Additional features and advantages of the present invention will become apparent to those skilled in the art upon consideration of the following detailed description of the illustrative embodiments exemplifying the best mode of carrying out the invention as presently perceived.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing aspects and many of the intended advantages of this invention will become more readily appreciated as the same becomes better understood by reference to the following detailed description when taken in conjunction with the accompanying drawings.

FIG. 1 is a perspective view of an exemplary cargo vehicle of the present disclosure, the cargo vehicle including a cargo body formed from a floor, a roof, right and left sidewalls, a nose, and a rear door assembly;

FIG. 2 is a perspective view of the floor of FIG. 1;

FIG. 3 is a perspective view of an exemplary mold assembly of the present disclosure, the mold assembly including a mold body, a base, and a frame;

FIG. 4 is a perspective view of the mold body of FIG. 3, the mold body including a plurality of segments;

FIG. 5 is front end elevational view of two adjacent segments from the mold body of FIG. 4;

FIG. 6 is another front end elevational view of the segments of FIG. 5, shown with the floor being molded upon the segments; and

FIG. 7 is a flow chart of an exemplary molding process of the present disclosure.

Corresponding reference characters indicate corresponding parts throughout the several views. Although the drawings represent embodiments of various features and components according to the present disclosure, the drawings are not necessarily to scale and certain features may be exaggerated in order to better illustrate and explain the present disclosure. The exemplification set out herein illustrates an embodiment of the invention, and such an exemplification is not to be construed as limiting the scope of the invention in any manner.

DETAILED DESCRIPTION OF THE DRAWINGS

For the purposes of promoting an understanding of the principals of the invention, reference will now be made to the embodiments illustrated in the drawings, which are described below. The embodiments disclosed below are not intended to be exhaustive or limit the invention to the precise form disclosed in the following detailed description. Rather, the embodiments are chosen and described so that others skilled in the art may utilize their teachings. It will be understood that no limitation of the scope of the invention is thereby intended. The invention includes any alterations and further modifications in the illustrative devices and described methods and further applications of the principles of the invention which would normally occur to one skilled in the art to which the invention relates.

1. Cargo Vehicle

Referring initially to FIG. 1, a cargo vehicle 100 is shown for supporting and transporting cargo. The illustrative vehicle 100 extends along a longitudinal axis L from a front end 102 to a rear end 104 and includes a motorized truck 106 that powers a plurality of wheels 108 or other traction devices. The illustrative vehicle 100 also includes a chassis 110 and a cargo body 120 formed from a plurality of panels, specifically a floor 130, a roof 140, right and left sidewalls 150, and a front wall or nose 160. The cargo body 120 also includes a rear door assembly 170 to provide access to the cargo body 120.

In the illustrated embodiment of FIG. 1, cargo body 120 is an enclosed body that is supported entirely atop chassis 110. Cargo body 120 may be refrigerated and/or insulated to transport temperature-sensitive cargo. While the concepts of this disclosure are described in relation to a refrigerated truck body, it will be understood that they are equally applicable to other vehicles generally, and more specifically to conventional trailers (e.g., dry freight semi trailers, refrigerated semi trailers), conventional truck and/or box or van type trailers (e.g., dry vans), examples of which include, but are not limited to, straight truck bodies, small personal and/or commercial trailers and the like. Accordingly, those skilled in the art will appreciate that the present invention may be implemented in a number of different applications and embodiments and is not specifically limited in its application to the particular embodiments depicted herein.

2. Composite Panels

Various panels of the cargo body 120 may be constructed, at least in part, of composite materials. For example, the floor 130, roof 140, right and left sidewalls 150, and/or nose 160 of the cargo body 120 may be constructed of composite materials. As such, the floor 130, roof 140, right and left sidewalls 150, and/or nose 160 of the cargo body 120, may be referred to herein as composite panels.

Composite structures are generally formed by combining two or more different constituents that remain separate and distinct in the final composite material. Exemplary composite materials include fiber-reinforced plastics (FRP), for example carbon-fiber reinforced plastics (CRP). These composite structures may lack internal metal components. Also, each composite panel may be a single, unitary component, which may be formed from a plurality of layers permanently coupled together, as discussed further below.

The composite construction of the cargo body 120 may present certain advantages. For example, the composite cargo body 120 may be lighter in weight than a typical metallic cargo body, which may improve fuel efficiency. Also, the composite cargo body 120 may have fewer metallic structures than a typical cargo body, which may make the cargo body 120 less susceptible to corrosion and heat loss. Additionally, the composite cargo body 120 may include fewer parts than a typical metallic cargo body, which may simplify construction, reduce inventory, and reduce variation in manufacturing. Further, the composite cargo body 120 may be suitable for use with sensitive cargo, including foodstuffs, because the composite materials may be inert to avoid reacting with the cargo and other materials and because the composite materials may be easy to clean and maintain to ensure proper hygiene. As a result, the composite cargo body 120 may qualify as “food grade” equipment.

Referring next to FIG. 2, the composite floor 130 of the cargo body 120 is shown in more detail. Although the following description pertains to the composite floor 130 of the cargo body 120, this description is also applicable to other composite panels of the cargo body 120, including the roof 130, right and left sidewalls 150, and/or nose 160. This description is also applicable to composite structures generally, including panels and other structures used to construct storage units, temporary shelters, shipping containers, boat hulls, airplane fuselages and wings, and furniture, for example.

The illustrative composite floor 130 is generally rectangular in shape and extends along the longitudinal axis L. of the vehicle 100 (FIG. 1). The composite floor 130 includes right and left sides 131 positioned adjacent to the right and left sidewalls 150 of the cargo body 120, a front end 132 positioned adjacent to the nose 160 of the cargo body 120, and a rear end 133 positioned adjacent to the rear door assembly 170 of the cargo body 120 (FIG. 1).

The composite floor 130 also includes an upper floor surface 134 and a lower floor surface 135. The upper floor surface 134 includes flat portions 136 for supporting cargo. The upper floor surface 134 may also include various longitudinal features that deviate from the flat portions 136 and extend parallel to the longitudinal axis L. For example, as shown in FIG. 2, the upper floor surface 134 includes a plurality of longitudinal channels 138 that are recessed into the otherwise flat upper floor surface 134, with flat portions 136 being located between adjacent channels 138. The upper floor surface 134 may also include longitudinal ridges (not shown) that are raised above the otherwise flat upper floor surface 134. The longitudinal channels 138 and ridges (not shown) may provide traction on the otherwise flat upper floor surface 134 to stabilize the cargo and reduce slippage. The longitudinal channels 138, in particular, may also accommodate electrical wiring, air lines, or other equipment for vehicle 100.

The size and shape of the composite floor 130 may vary to accommodate different vehicles 100. In the illustrated embodiment of FIG. 2, the composite floor 130 has a width w_(f) between the right and left sides 131 of about 8.5 feet, a length l_(f) between the front end 132 and the rear end 133 of about 34 feet, and a thickness t_(f) between the upper floor surface 134 and the lower floor surface 135 of about 4 inches. However, the composite floor 130 may have a width w_(f) of about 8-12 feet, a length l_(f) of about 12-60 feet, and a thickness t_(f) of about 1-8 inches, for example.

Additional information regarding composite structures is disclosed in the following patents and published patent applications, each of which is incorporated by reference in its entirety herein: U.S. Pat. Nos. 5,429,066, 5,800,749, 5,664,518, 5,897,818, 6,013,213, 6,004,492, 5,908,591, 6,497,190, 6,911,252, 5,830,308, 6,755,998, 6,496,190, 6,911,252, 6,723,273, 6,869,561, 8,474,871, 6,206,669, and 6,543,469, and U.S. Patent Application Publication Nos. 2014/0262011 and 2014/0199551. Exemplary composite structures include DuraPlate® structures provided by Wabash National Corporation of Lafayette, Ind. and PRISMA® structures provided by Compsys, Inc. of Melbourne, Fla.

3. Mold

Referring next to FIGS. 3-6, a mold assembly 300 is provided for manufacturing the composite floor 130 of the cargo body 120 (FIG. 1). In the case of vehicle 100, similar molds may be provided for manufacturing other composite panels of the cargo body 120, such as the roof 140, right and left sidewalls 150, and/or nose 160 (FIG. 1). In the case of other composite structures, such as the above-mentioned storage units, temporary shelters, shipping containers, boat hulls, airplane fuselages and wings, and furniture, similar molds may also be provided for manufacturing those composite structures.

The illustrative mold assembly 300 includes a mold body 310, a base 330, and a frame 340 having castor wheels 342 to facilitate movement of the mold assembly 300. The mold assembly 300 may also include brackets (not shown) to facilitate lifting and transporting the mold assembly 300, such as using a crane.

As shown by comparing FIG. 4 with FIG. 2, the mold body 310 of FIG. 4 generally corresponds in size and shape to the resulting composite floor 130 of FIG. 2. The mold body 310 is generally rectangular in shape and extends along the longitudinal axis L. The mold body 310 includes right and left sides 311 that correspond to the right and left sides 131 of the resulting composite floor 130, a front end 312 that corresponds to the front end 132 of the resulting composite floor 130, and a rear end 313 that corresponds to the rear end 133 of the resulting composite floor 130. The mold body 310 has a width w_(m) between the right and left sides 311 that is equal to or greater than the width w_(f) of the resulting composite floor 130. The mold body 310 has a length l_(m) between the front end 312 and the rear end 313 that is equal to or greater than the length l_(f) of the resulting composite floor 130.

The mold body 310 also includes an upper mold surface 314 and a lower mold surface 315. The upper mold surface 314 is a negative mold for the resulting upper floor surface 134, such that the upper floor surface 134 can be formed upon the upper mold surface 314, as discussed further below. The upper mold surface 314 includes flat portions 316. Any unintended gaps or defects in the upper mold surface 314 may be filled with a suitable filler 317 (e.g., metal rods, wax) to provide this flat surface. The upper mold surface 314 may also include various longitudinal features that deviate from the flat portions 316 and extend parallel to the longitudinal axis L to form the opposite longitudinal features in the upper floor surface 134. For example, as shown by comparing FIG. 4 with FIG. 2, the upper mold surface 314 includes longitudinal ridges 318 that form corresponding longitudinal channels 138 in the otherwise flat upper floor surface 134. The upper mold surface 314 may also include longitudinal channels (not shown) that would form corresponding longitudinal ridges (not shown) in the otherwise flat upper floor surface 134.

Between the upper mold surface 314 and the lower mold surface 315, the mold body 310 may be substantially hollow except for a plurality of spaced-apart internal supports 319. The hollow construction of the mold body 310 may accommodate a heat exchange fluid (e.g., air, water) inside the mold body 310 to control the temperature of the upper mold surface 314 during molding, as discussed further below.

According to an exemplary embodiment of the present disclosure, the mold body 310 is formed by extrusion along the longitudinal axis L from the front end 312 to the rear end 313. More specifically, the mold body 310 may be formed by passing material through a die along the longitudinal axis L, where the die has a desired cross-section in a direction perpendicular to the longitudinal axis L. As such, the mold body 310 may be referred to herein as an “extruded” mold body 310. Because the features in the upper mold surface 314 of the mold body 310 (e.g., the flat portions 316, the ridges 318) are also formed by extrusion, these features may extend along the longitudinal axis L entirely from the front end 312 to the rear end 313. The mold body 310 may be constructed of metal (e.g., aluminum) or another material that is suitable for extrusion.

To accommodate standard extrusion equipment, the mold body 310 may be divided into a plurality of individually extruded segments 320 across the width w_(m). The illustrative mold body 310 includes nine segments 320, with each segment 320 accounting for 1/9 of the width w_(m) but this number may vary. The width w_(s), of each segment 320 may be about 0.5-2 feet, and the length l_(s) of each segment may be the same as the overall length l_(m) of the mold body 310 itself. For simplicity of construction, the segments 320 may be identical to one another and trimmed to the desired length.

FIG. 5 shows two adjacent segments of mold body 310—a left segment 320L and a right segment 320R. The segments 320L, 320R are placed side by side and coupled together to form the mold body 310. Adjacent segments 320L, 320R may be coupled directly together through mechanical fastening, welding, and/or adhesive bonding, for example. Also, adjacent segments 320L, 320R may include interconnecting features. For example, in the illustrated embodiment of FIG. 5, the left side of each segment 320L, 320R includes a protrusion 322, and the right side of each segment 320L, 320R includes a recess 324 that is configured to receive the adjacent protrusion 322. In certain embodiments, this connection may be tight and secure, like a snap connection, such that the interconnecting features are configured to physically hold the adjacent segments 320L, 320R together. Adjacent segments 320L, 320R may also be indirectly coupled together through the base 330 (FIG. 3). For example, if the base 330 is constructed of plywood, each segment 320L, 320R may be screwed to the base 330. The filler 317 may be used between adjacent segments 320L, 320R to provide a flat upper mold surface 314.

The extruded construction of the mold body 310 may present certain advantages. First, the extruded mold body 310 may be less expensive than a machined mold body. Second, the extruded mold body 310 may be more durable than a cast (e.g., fiberglass) mold body. Third, the extruded mold body 310 may be repaired, if necessary, such as by removing and replacing a damaged segment 320 while retaining the other segments 320. Finally, the profile of the upper mold surface 314 may be customized to create desired features in the upper floor surface 130 (FIG. 2).

4. Molding Process

Referring next to FIGS. 6 and 7, an exemplary molding process 700 is provided for manufacturing the composite floor 130 using the mold assembly 300.

In step 702, the upper mold surface 314 of the mold body 310 may be prepared for molding. For example, the upper mold surface 314 may be cleaned and/or pretreated with a release agent (e.g., wax) to facilitate separation after molding.

In step 704, a first resin layer 600 is applied onto the upper mold surface 314 of the mold body 310. An exemplary first resin is a gel coat polyester resin. The first resin layer 600 may be applied across the mold body 310 in liquid form by spraying, rolling, brushing, or calendaring, for example. The first resin layer coats the negative space above the upper mold surface 314.

In step 706, the first resin layer 600 is allowed to cure using a suitable curing catalyst. Ultimately, the first resin layer 600 will take on the opposite profile of the upper mold surface 314 to form the upper floor surface 134 of the composite floor 130.

In step 708, one or more reinforcing materials 604 are applied onto the cured first resin layer 600 from step 706. Exemplary reinforcing materials 604 include woven or stitched fiberglass cloth sheets, for example. Other exemplary reinforcing materials 604 include extruded preform assemblies of a woven or stitched fiberglass cloth, a non-woven spun bond polymeric (e.g., polyester) material, and a polymeric (e.g., polyurethane) foam core, for example. The spun bond polymeric material may be mechanically stitched to the fiberglass cloth and/or the foam. In one embodiment, the spun bond material may be a polyester material, the foam may be a polyurethane material, and the resin may be a thermoset plastic resin matrix. Such preforms and any other reinforcing materials 604 may be shaped, cut to size, and arranged on the mold assembly 300 in a manner that accommodates the strength requirements of the final structure. In areas of the final structure requiring less strength, the preforms may be relatively large in size, with the foam cores spanning relatively large distances before reaching the surrounding fiberglass and polymeric skins. By contrast, in areas of the final structure requiring more strength, the preforms may be relatively small in size, with the foam cores spanning relatively small distances before reaching the surrounding fiberglass and polymeric skins. For example, the preforms may be shaped as relatively wide panels in areas of the final structure requiring less strength and as relatively narrow support beams in areas of the final structure requiring more strength. Other exemplary techniques for strengthening such support beams include reinforcing the outer skins, such as by using uni-directional glass fibers or additional cloth in the outer skins, and/or reinforcing the inner cores, such as by using hard plastic blocks or higher density foam in the inner cores.

In step 710, a second liquid resin layer 602 is applied and worked into the reinforcing materials 604 to wet the reinforcing materials 604 with the second resin 602. An exemplary second resin is a polyester resin, which may be similar to the first resin. An exemplary resin is the co-cure resin disclosed in U.S. Pat. No. 9,371,468, which is incorporated by reference in its entirety herein.

In step 712, the reinforced second resin layer 602 is allowed to cure using a suitable curing catalyst. During curing, the reinforcing materials 604 may be forced into close contact with the second liquid resin layer 602 by applying pressure on top of the reinforcing materials 604 and/or by applying a vacuum to the reinforcing materials 604, for example. Once cured, the second resin layer 602 becomes permanently coupled to the reinforcing materials 604 and the first resin layer 600 to form a single structure. Steps 708-712 may be repeated one or more times. In certain embodiments, the first curing step 706 may be performed together with the second curing step 712. In other words, the curing steps 706, 712 may be performed simultaneously.

In step 714, a third resin layer 606 may be applied onto the cured second resin layer 602. An exemplary third resin is a polyester resin, which may be similar to the first and/or second resins.

In step 716, the third resin layer 606 is allowed to cure using a suitable curing catalyst. Once cured, the third resin layer becomes permanently coupled to the first resin layer 600 and second resin layer 602 to form a single structure. Ultimately, the third resin layer 606 may form the lower floor surface 135 of the composite floor 130. It is also within the scope of the present disclosure for the third resin layer 606 to be eliminated and for the reinforced second resin layer 602 to form the lower floor surface 135 of the composite floor 130. In certain embodiments, the first curing step 706 and the second curing step 712 may be performed together with the third curing step 716. In other words, the curing steps 706, 712, 716 may be performed simultaneously.

In step 718, the composite floor 130 is removed from the mold body 310 and flipped over 180 degrees such that the upper floor surface 134 that was facing downward toward the mold body 310 now faces upward. If necessary, the outer perimeter of the composite floor 130 may be trimmed to desired dimensions for use in vehicle 100 (FIG. 1).

As indicated above, a heat exchange fluid (e.g., air, water) may be introduced (e.g., pumped) into the hollow mold body 310 to control the temperature of the upper mold surface 314 during the molding process 700. For example, to slow down or otherwise control a curing step 706, 712, 716, a cold heat exchange fluid may be introduced into the hollow mold body 310. Using a cold heat exchange fluid may be particularly beneficial when the curing step 706, 712, 716, is exothermic, because the cold heat exchange fluid may remove excess heat and maintain a controlled curing temperature. To speed up or otherwise control a curing step 706, 712, 716, a hot heat exchange fluid may be introduced into the hollow mold body 310. The temperature of the mold body 310 may also be controlled by placing the mold body 310 inside a temperature-controlled environment, such as a large refrigerator, oven, or autoclave, for example. The heat exchange fluid may be circulated repeatedly through the mold body 310 as part of a heat exchange loop.

Although the illustrative mold assembly 300 of FIG. 6 is an open mold that forms the upper floor surface 134 of the composite floor 130, it is also within the scope of the present disclosure for the mold assembly 300 to form other surfaces of the composite floor 130. For example, the mold assembly 300 may be a closed mold that forms the right and left sides 131, the front end 132, the rear end 133, the upper floor surface 134, and/or the lower floor surface 135 of the composite floor 130. The mold assembly 300 may include one or more mold bodies 310, some or all of which may be extruded. For example, the mold assembly 300 may have upper and lower mold bodies that interact to form the composite floor 130 therebetween. One or both of the upper and lower mold bodies may be extruded.

The closed-molding method may be similar to the open-molding method of FIG. 7 with certain differences, as noted herein. The reinforcing materials may be placed inside the mold assembly 300 before the resin. With the mold assembly 300 closed, the resin may be introduced into the mold assembly 300, such as by injecting the resin into the mold assembly 300 and/or pulling the resin into the mold assembly 300 using a vacuum. Then, the mold assembly 300 may be compressed, such as by using vacuum pressure, mechanical pressure, and/or water pressure, to form the composite floor 130 inside. Finally, the mold assembly 300 may be opened to reveal the composite floor 130.

While this invention has been described as having an exemplary design, the present invention may be further modified within the spirit and scope of this disclosure. This application is therefore intended to cover any variations, uses, or adaptations of the invention using its general principles. Further, this application is intended to cover such departures from the present disclosure as come within known or customary practices in the art to which this invention pertains. 

1. A mold used to form a composite structure, the mold comprising: an extruded mold body comprising a plurality of independent mold body segments coupled together, the plurality of mold body segments defining a mold surface upon which the composite structure is directly formed, the plurality of mold body segments including: a first extruded mold body segment having an upper surface, a lower surface opposite the upper surface, and at least one internal support extending between the upper surface and the lower surface; and a second extruded mold body segment having an upper surface, a lower surface opposite the upper surface, and at least one internal support extending between the upper surface and the lower surface, wherein the upper surface of the first extruded mold body segment and the upper surface of the second extruded mold body segment cooperate to define the mold surface.
 2. The mold of claim 1, wherein the mold body has a width of about 8-12 feet and a length of about 20-50 feet.
 3. (canceled)
 4. The mold of claim 1, wherein each of the mold body segments extends an entire length of the mold body and a partial width of the mold body.
 5. The mold of claim 1, wherein each of the mold body segments has a width of about 0.5-2 feet.
 6. The mold of claim 1, wherein the plurality of mold body segments are identical to each other.
 7. The mold of claim 1, wherein the mold body is constructed of aluminum.
 8. The mold of claim 1, wherein each of the first and second extruded mold body segments includes a hollow portion configured to receive a heat exchange fluid.
 9. The mold of claim 1, wherein the mold surface includes: a first portion that is flat; a second portion that is flat; and a third portion that deviates from being flat, wherein the third portion extends parallel to a longitudinal axis of the extruded mold body.
 10. The mold of claim 9, wherein the third portion is a channel that is recessed between the first and second portions.
 11. The mold of claim 9, wherein the third portion extends entirely from a first end to a second end of the mold body.
 12. (canceled)
 13. A composite panel formed directly upon the mold body of claim 1, the composite panel comprising: a first end; a second end; and a molded surface including: a first portion that is flat; a second portion that is flat; and a third portion that deviates from being flat, wherein the third portion extends entirely from the first end to the second end.
 14. The composite panel of claim 13, wherein the composite is a fiber-reinforced plastic.
 15. The composite panel of claim 13, wherein the mold body is extruded along a longitudinal axis, and the third portion extends parallel to the longitudinal axis.
 16. The composite panel of claim 13, wherein the third portion is a channel that is recessed between the first and second portions.
 17. The composite panel of claim 13, wherein the composite panel is one of a floor, a roof, a sidewall, and a nose for a cargo vehicle.
 18. (canceled)
 19. (canceled)
 20. (canceled)
 21. The mold of claim 1, wherein: the upper surface and the lower surface of the first extruded mold body segment are parallel; and the upper surface and the lower surface of the second extruded mold body segment are parallel.
 22. The mold of claim 1, wherein the upper surface of the first extruded mold body segment and the upper surface of the second extruded mold body segment are co-planar.
 23. The mold of claim 1, wherein each of the first and second extruded mold body segments include a plurality of internal supports extending between the upper surface and the lower surface of the respective one of the first and second extruded mold body segments.
 24. The mold of claim 23, wherein the first extruded mold body segment includes at least one internal passageway defined by adjacent ones of the plurality of internal supports, the at least one internal passageway configured to receive a heat exchange fluid. 